REVIEW ARTICLE
Year : 2022  |  Volume : 11  |  Issue : 1  |  Page : 7

The effect of various nanoparticle coating on the frictional resistance at orthodontic wire and bracket interface: A systematic review


1 unior Resident, Faculty of Dental Sciences, IMS BHU, Varanasi, UP, India
2 Associate Professor, Faculty of Dental Sciences, IMS BHU, Varanasi, UP, India
3 Professor, Faculty of Dental Sciences, IMS BHU, Varanasi, UP, India

Date of Submission06-Jun-2021
Date of Decision24-Jul-2021
Date of Acceptance10-Nov-2021
Date of Web Publication04-May-2022

Correspondence Address:
Vipul K Sharma
Faculty of Dental Sciences, IMS BHU, Varanasi, UP – 221005
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/jos.jos_152_21

Rights and Permissions
  Abstract 


This systematic review was aimed to test the null hypothesis that coating of orthodontic wires with nanoparticles does not affect the frictional properties at bracket--wire interface. Electronic database searches were performed up to September 2020. In vitro studies were considered for reviewing process. Study selection, data extraction, risk of bias assessment was performed during reviewing process. Only qualitative analyses of included literature were done due to the presence of heterogeneity among the studies. Out of 1,068 retrieved records, nine studies satisfied the inclusion criteria and included in this review. Studies were assessed at low risk to high risk of bias according to certain parameters. Wide variety of nanoparticles were used for surface coating of orthodontic wires of variable sizes, shapes, and materials like stainless steel, NiTi, and TMA and placed into the slots of different types of orthodontic brackets to evaluate the alteration in frictional and other mechanical properties. Most of the studies clearly indicate that coating with nanoparticles decreases the friction between wire and bracket interface under specified in vitro conditions. Furthermore, among the nine included studies, only two considered evaluation of effect of coated brackets on frictional and other mechanical properties and results were heterogeneous. The null hypothesis is rejected and it is concluded that the wires coated with nanoparticles might offer a novel opportunity to substantially reduce frictional resistance at bracket--wire interface during tooth movement. Further studies are necessary to strengthen the evidence regarding effect of coated brackets on frictional properties.

Keywords: Coating methods, frictional properties, nanoparticles, orthodontic brackets, orthodontic wires


How to cite this article:
Indumathi P, Singh D, Sharma VK, Shukla NK, Chaturvedi T P. The effect of various nanoparticle coating on the frictional resistance at orthodontic wire and bracket interface: A systematic review. J Orthodont Sci 2022;11:7

How to cite this URL:
Indumathi P, Singh D, Sharma VK, Shukla NK, Chaturvedi T P. The effect of various nanoparticle coating on the frictional resistance at orthodontic wire and bracket interface: A systematic review. J Orthodont Sci [serial online] 2022 [cited 2022 Sep 27];11:7. Available from: https://www.jorthodsci.org/text.asp?2022/11/1/7/344720




  Introduction Top


Over the past 100 years, improvements in the field of mechanotherapy and treatment philosophy have largely been made possible with the emergence of newer orthodontic materials. Archwire materials form a larger part of this change, and a thorough knowledge of biomechanical and clinical applications of the archwire is required for selecting the same. Several properties such as esthetics, friction, biostability, formability, weldability, resilience and spring back, etc., should be considered during the search of an ideal archwire. Friction plays an important role among the alloy's characteristics that alter the behaviour of the archwire.

During alignment and space closure in the dental arch, sliding a tooth along an orthodontic wire is a common clinical procedure. Whenever sliding occurs, a frictional force is generated between the wire and the orthodontic bracket.[1] “Friction is defined as the resisting force tangential to the common boundaries between two or more bodies, when under the action of an external force, one body moves or tends to move relative to the surface of the other”.[2] In 1976, Farrant et al.[3] briefly described role of friction in orthodontics as teeth are moved via a traction force along an archwire. In case of orthodontic mechanotherapy, a biological tissue response with resultant tooth movement will occur only when the applied forces adequately overcome the friction at the bracket--wire interface.[4] The lost portion of the applied force (because of the resistance to sliding) can range from as low as 12% to as high as 60%.[5] High frictional forces will affect the efficiency of the system severely, and this leads to the extension of treatment time or the outcome becomes compromised because of little or no tooth movement.

In 1992, Kusy et al.,[6] made attempts to alter or modify the surface properties of orthodontic materials assuming the interaction of the surface chemistry of the bracket slot with the archwire may affect the friction. Surface films are most powerful modifiers of friction and it can change friction by as much as factor of 10.[7],[8] To improve the tribological properties, various surface treating techniques have been applied on the orthodontic appliances with the evolution in the material engineering. The objective of this systemic review was to resolve the null hypothesis that coating of orthodontic wires does not have any effect on frictional properties at bracket--wire interface.


  Materials and Methods Top


This systematic review was conducted according to well-established guidelines of PRISMA (Preferred Reporting Items for Systematic Review and Meta-Analysis) and Cochrane Handbook of systematic review.[9],[10] Protocol was constructed according to recommended guidelines but no registration was performed on publicly accessible database.

Search strategy

An electronic search of scientific literature was performed without restriction to time and language. All the original research articles, review articles, published bibliographies, unpublished research works and relevant citations related to surface modification of orthodontic wires were checked for relevant information, used in this review. Reference list of included studies were also explored for any relevant articles. Electronic and manual search were conducted on database including PubMed, Scopus, Science direct, Google scholar, and Web of science up to September 2020. A combination of search terms “Orthodontic wires,” “NiTi wires,” “Stainless steel wires,” “Beta Titanium wires,” “coated orthodontic wires,” “frictional behavior of orthodontic wires,” “mechanical properties of coated wires,” “surface modification of orthodontic wires” and “surface characteristic of coated orthodontic wire” were used.

Eligibility criteria (PICOS scheme)

Participants (Specimen)

  • In vitro studies involving surface modification of received orthodontic wires and brackets by nanoparticles to improve frictional properties and other mechanical/physical properties.


Intervention

  • Studies describing the specific coating method used for surface modification of orthodontic wires.


Comparison

  • Studies comparing coated wire's frictional and other mechanical properties with control group (uncoated wire).


Outcome

  • Changes in frictional properties as a primary outcome, while other mechanical properties as a secondary outcome.


Study design

  • In vitro studies.


Exclusion criteria

  • Case reports, preliminary reports, case series, letter to editor, comments, repetitive publications, systematic review and abstracts.
  • Studies evaluating frictional properties without control group.
  • Studies done on retrieved wires after clinical use.
  • Studies involving coating done for esthetic purposes.
  • Studies considering biological properties of surface modified orthodontic wires.


Study selection and data extraction

Abstracts of the retrieved results were scrutinized, and papers that seemed to meet the initial selection criteria defined (in vitro studies that addressed surface modification by coating nanoparticles to improve frictional properties of orthodontic wires) were identified. Papers were excluded at this stage if they were descriptive, editorial, letter to editor, in vivo, or were studying other properties of surface modified orthodontic wires rather than friction. Full articles were obtained from the abstracts/titles that met the inclusion criteria. The selections were then discussed, and discrepancies were resolved. Furthermore, a secondary (manual) search was then performed by going through the reference lists of the selected articles to identify any paper that met the inclusion criteria but was missed by the electronic searches.

Risk of bias assessment

Two authors (NKS and VKS) independently evaluated the risk of bias of each included study considering a score described in previous systematic reviews of in vitro studies.[11],[12] The description of the following parameters was checked in each study: randomization of the specimens for experimental and control groups, prior sample size calculation, similar cross-section or size of specimen, intervention defined, control group taken, statistical analysis performed, blinding of observer, commercial or noncommercial specimen specified, all possible outcome reported or not, loss of specimen reported or not. If the parameter was described on the text, the study received a “yes” on that specified parameter; otherwise, it had a “no”. The risk of bias was classified according to the sum of “yes” received as follows: 1–3 = high, 4–5 = moderate, 6–10 = low risk of bias. Unclear and no information entries were considered as of some concern if domain question seems to affect the outcome of the study otherwise marked under low-risk category accordingly. Any disagreements were resolved by discussion with other three authors (IMP, TPC and DS).

Synthesis of result

Studies were considered for quantitative analysis if presented with sufficient homogenous data with respect to participants, intervention and outcomes. Otherwise, qualitative assessment of the data would have been undertaken. Data on the alteration of frictional and mechanical properties due to application of different coating materials were planned to be expressed as risk ratios (RR) for dichotomous data and standardized mean difference (SMD) for continuous data, together with the relevant 95% confidence intervals (CI). Random effect model was planned to combine the data.


  Results Top


Study selection

The search results based on electronic search yielded 1,068 articles initially. After exclusion of duplicates, 953 studies remained. After screening of titles and abstracts 924 articles were scrutinized against the selection criteria. Then, the full text of 29 articles were obtained and assessed for eligibility, after applying the eligibility criteria. A total of 9 publications were finally included in this systematic review. References and citations of final included articles were also explored for any relevant studies. The flow chart summarizing the search strategy is provided in [Figure 1].
Figure 1: Flowchart diagram of search strategy, according to PRISMA guideline)

Click here to view


Characteristics of included studies

The characteristics of various studies are mentioned in [Table 1]. A wide variety of nanoparticles were used for surface coating of orthodontic wires that include Diamond like carbon (DLC), Fullerene like nanoparticles of tungsten disulfide (IF-WS2), Spherical Zinc oxide (ZnO), Titanium aluminium nitride (TiAlN), tungsten carbide (WC/C), Molybdenum and tungsten disulfide (IF-WS2) and nanoparticles of silver (Ag). All the included studies conducted in vitro experiment by manual coating of orthodontic wires with description of the specific coating method. Nanoparticles after coating were evaluated by scanning electron microscope (SEM) associated with X-ray diffractometry and X-ray spectrometry. Most of the studies employed universal testing machine to carry out mechanical measurements such as friction, load deflection and elastic modulus for coated and uncoated wires.
Table 1: Characteristics of various studies

Click here to view


Results of individual studies and qualitative synthesis

Due to presence of heterogeneous data with respect to participants, interventions and outcomes, only qualitative analysis of the data has been done. Differences were observed in the following variables- Coating material and method, Wires used with respect to dimension and type, Bracket type and prescription, force applied, load cell, and weight, Bracket--wire angulations. Results of the individual in vitro studies to evaluate friction and other properties are reported in [Table 2] and details of the outcome of frictional measurements are enumerated in [Table 3]. For the descriptive purpose, outcomes were divided into following categories.
Table 2: Overall result of individual studies

Click here to view
Table 3: Result of individual studies to evaluate friction

Click here to view


Different coatings and friction. Among the included studies three of them used fullerene like nanoparticles of tungsten disulfide which were deposited on different wire combinations.[13],[14],[15] One study[13] used fullerene like nanoparticles of nickel-phosphorous (Ni-P) and tungsten disulfide (IF-WS2) for coating stainless steel archwires and the results showed that the coated archwires exhibited a significant reduction of the frictional force. Another study[14] which used Cobalt (Co) and fullerene like tungsten disulfide (IF-WS2) for coating on nickel titanium archwires demonstrated a decline of static and kinetic friction coefficients with respect to the uncoated wires. Gracco et al.[15] incorporated nanoparticles of molybdenum (MoS2) and tungsten disulfide (WS2) and the wires coated with Ni + MoS2 (Nickel + molybdenum) and Ni + WS2 (Nickel + tungsten disulfide) films have friction values significantly lower than uncoated wires. DLC (diamond like carbon) nanoparticles were used in three studies.[16],[17],[18] All the three studies reported that the frictional values are lower than the uncoated wires. Zhang et al.[17] reported that the kinetic friction coefficient of DLC-coated wires were reduced compared with the control wires but the static friction coefficient of the nitro-carbarized wires was significantly lower than those of the DLC-coated wires and uncoated wires. One study[19] used ZnO (Zinc oxide) nanoparticles for surface modification and showed that deposition of ZnO on stainless steel wires does not affect the frictional properties. Krishnan et al.[20] used TiAlN (titanium aluminium nitride) and WC/C (tungsten carbide) for coating and the results indicated that frictional properties of WC/C-coated wires were reduced compared with TiAlN coated and uncoated wires. Another study[21] used nanoparticles of silver (Ag) as coating material and revealed that the silver coated wire did not show any change in the frictional resistance when compared with uncoated wire.

Friction in stainless steel archwires. Most of the included studies got the measure of frictional resistance of coated stainless steel archwires. Among them, 5 studies[13],[15],[16],[17],[18] substantiated that stainless steel archwires when coated with nanoparticles such as DLC and fullerene like nanoparticles resulted in lower frictional forces and other 2 studies validated that stainless steel archwires showed no improvement in frictional characteristics when coated with nanoparticles such as ZnO[19] and Ag.[21] Only one study[16] coated DLC nanoparticles on both stainless steel and nickel titanium wires and revealed that DLC coated stainless steel wires exhibited significantly less frictional force.

Friction in Nickel titanium archwires. Two studies[14],[16] evaluated the frictional resistance of coated nickel titanium wires. One study[14] used fullerene like tungsten disulfide and the other study[16] used DLC nanoparticles. Both of them revealed that there is improvement in frictional force after coating when compared with uncoated wires.

Friction in other archwires. Only one study[20] deposited TiAlN and WC/C tungsten carbide over beta titanium wires and reported that WC/C coated wires had reduced frictional forces when compared with TiAlN coated and uncoated wires.

Wire and bracket combination. Only two of the nine studies investigated the effect of nanoparticle coating on brackets in frictional resistance.[18],[19] One study[18] coated DLC nanoparticle on stainless steel brackets and conveyed that DLC coated brackets when combined with DLC coated wires exhibited a reduction in frictional force otherwise DLC coated brackets alone does not affect the frictional resistance. Another study[19] which coated ZnO nanoparticles on ceramic brackets revealed that the presence of ZnO nanoparticle coating on ceramic brackets was effective in terms of frictional resistance than the coating on wire. According to Muguruma et al.,[16] self-ligating brackets showed significantly less frictional force than the conventional brackets when combined with coated wires. Gracco et al.,[15] in their study, employed two kinds of self-ligating brackets that is interactive (In-Ovation) and passive (Damon-Q) self-ligating brackets and the results suggested that interactive self-ligating brackets gave better performance than passive self-ligating brackets in terms of friction.

Other reported outcome. On observing the evaluation of other properties other than friction, Zhang et al.[17] reported that after surface modification, microhardness of the DLC-coated wires (685.17 Hv) was increased 1.46 times compared with the control wires (468.42 Hv). On the other hand, the elastic modulus for the DLC-coated stainless steel wire was less than that of the as-received stainless steel wire [277.39 ± 16.33Gpa (uncoated S. S wire) 194.44 ± 9.09Gpa (DLC coated S. S wire)]. Surface hardness were not evaluated for other nanoparticles. As reported by Krishnan et al.,[20] the load deflection rate was significantly reduced by both TiAlN and WC/C coating [2.90 ± 0.141 (uncoated) 1.612 ± 0.029 (TiAlN coated) 1.56 ± 0.054 (WC/C coated)].

Risk of bias in individual studies

Risk of bias assessment was evaluated under 10 specific domains. [Table 4] explains risk of bias assessment in individual studies. Most of the studies[13],[15],[16],[17],[18],[19],[20] concluded at moderate risk of bias except Shah et al.,[21] which was concluded at low risk and Samorodnitzky et al.,[14] at high risk of bias. The items that most frequently received “no” in the analysis were: the randomization of specimens, loss of any specimen reported, and description of sample size calculation. In addition, all studies uniformly received “no information” entry under the description manufactures' instruction followed, and the presence of an operator blinded to experimental condition.
Table 4: Risk of bias assessment

Click here to view



  Discussion Top


Significance of frictional force is apparent in sliding mechanics because this retarding factor reduces the amount of force employed by the fixed appliance for the desired tooth movement. Friction reduction would allow the application of a lower orthodontic force, with significant benefits, ranging from a lower risk of root resorption, to the best anchorage control, and reduction of the treatment time. Orthodontic research has been focussing in finding a solution to this problem with the support of material engineering. However, the most significant progress is being achieved with application of nanotechnology to the orthodontic archwires. In particular, coating orthodontic wires with nanoparticles is the best way to achieve better results in researches which were aimed at the reduction of friction. The inorganic fullerene-like tungsten disulphide (IF-WS2) nanoparticles were described first in 1992.[22] The size of these nanoparticles ranges from 20 to 200 nm depending on the tungsten oxide (WO3) precursor size. Synthesis of fullerene-like WS2 nanoparticles has allowed remarkable improvement of frictional behaviour and wear properties under different conditions.[23] Solid lubricants of WS2 nanoparticles penetrate into the interface between the rubbed surfaces which results in low friction and wear.

Three studies included in this systematic review used this fullerene-like nanoparticles with different combinations.[13],[14],[15] 17--54% reduction of frictional resistance was obtained by coating the wire with nickel-phosphorous electroless films impregnated with inorganic fullerene-like nanoparticles of tungsten disulfide (IF-WS2). The results obtained were in agreement with the study which showed that electroless platting of Ni-P and IF-WS2 of a carbon steel substrate displayed excellent friction and wear properties due to their unique fullerene-like structure.[24] Tribology data obtained from the cobalt and IF-WS2 coated NiTi wires demonstrated 22--34% reduction of frictional forces.[14] Both the studies showed that a substantial reduction in the frictional force was recorded at the highest angle and these findings were consistent with previous studies.[25],[26] Reason behind this is when the angle increases, load at the edges of the slot increases, causing a higher friction level on the uncoated wire. At this point, coated wires exfoliate some of the nanoparticles resulting in lubrication of the sliding. Models suggested by Rapoport et al.[23] and Cash A et al.[27] explains the mechanism by which there is an achievement of reduced friction, Corroboration with the results obtained with the previous studies, Gracco et al.[15] also observed that improvements in terms of friction were obtained with coatings incorporating MoS2 and WS2. Friction reduction is primarily due to the “buffer” like action carried out by the nanoparticles, which flow between the surfaces, maintaining their shape. In high load conditions, nanoparticles induce the formation of a deposit at the level of surface roughness, reducing the direct contact between the asperities and minimizing wear.

Recently, DLC coating is becoming increasingly important in orthodontic applications owing to its superior properties.[28],[29] These nanoparticles are expected to offer the potential of greatly improving frictional properties. Muguruma et al.[16] have investigated the effect of DLC coating on the static frictional force of stainless steel and nickel titanium orthodontic archwires and found that DLC coating process reduced the frictional force under dry conditions. In this study, although the stainless steel wires showed smoother and harder surface characteristics than the nickel--titanium wire, the stainless steel wires had greater frictional forces than the nickel--titanium wires. The stainless steel archwires had wider cross-sectional dimensions and a higher value of the elastic modulus than the nickel--titanium wires, and this should have affected binding and notching. Kang et al.[18] investigated the frictional behaviour of DLC-coated archwires and brackets by using self-developed tester in ambient air of artificial saliva. Conventional archwires and brackets without DLC coating had lower friction coefficients in artificial saliva than they were in ambient air. However, no correlation was found between applied environment and friction coefficient for the DLC-coated wires. The results confirm that the saliva medium tends to decrease the friction coefficient for the uncoated wires, by favouring the lubrication of the interface, but it does not affect the friction coefficient for the DLC-coated wires.[30],[31] Nevertheless, the DLC-coated and uncoated brackets showed no significant differences in the friction coefficient. This is not consistent with previous report of Muguruma et al.,[32] as they showed that DLC-coated brackets showed significantly less kinetic frictional force than as-received brackets. In addition to the improvement in frictional characteristics of DLC-coated archwires Zhang et al.[17] found that after surface modification, microhardness of the DLC-coated archwires was increased 1.46 times compared with the control group and the nanoindentation test revealed that the elastic modulus of the DLC-coated wires obtained was significantly lower than that of the control wires. DLC-coated wires with a lower elastic modulus might show superior flexibility, which is a desirable characteristic of an orthodontic wire. DLC films are harder than most metallic materials with hardness values ranging from 6 GPa to 20 GPa depending on the deposition conditions.[33],[34]

One study[19] evaluated the effect of ZnO nanoparticles coating on stainless steel archwires and porcelain brackets and presented that ZnO nanoparticles coating on porcelain brackets was more effective than coating on wire. This can be contributed to the surface properties of porcelain brackets.[35] Since the high surface roughness of porcelain brackets is an important factor in the determination of frictional forces, modification of such surface may have potential to reduce the sliding friction and covering the wire with ZnO nanoparticles did not result in major changes in frictional forces and these results were consistent with study conducted by Kachoei et al.[36]

Shah et al.[21] quantitatively assessed the effect of silver coating on frictional resistance of SS wires and suggested that there was no statistically significant difference in frictional resistance between silver coated and uncoated wires. But SS wires showed significantly less frictional force in silver coated larger dimension wire (0.019“×0.025”) and this can be due to the difference in the play of smaller (0.017“×0.025”) and larger dimension (0.019“×0.025”) wires.[33] Krishnan et al.,[20] evaluated frictional properties, behavior and surface analysis, mechanical testing, microstructure and elemental analysis of TiAlN and WC/C coatings on titanium-molybdenum (TMA) orthodontic archwires. This study clearly indicated the superior nature of WC/C coated orthodontic archwires over uncoated and TiAlN coated archwires, exhibiting reduced frictional forces to sliding mechanics.

Two studies[15],[18] compared the frictional behaviour of self-ligating brackets in combination with coated wires. The self-ligating brackets has basic advantages, as they eliminate the need of certain utilities or materials such as elastomeric modules, along with the process or tools associated with their application. In addition, it has been proposed that due to bracket--wire engagement, light forces and reduced friction can be attained with a desirable outcome on the rate of orthodontic tooth movement. Both the study concluded that self-ligating brackets produced significantly less frictional forces than conventional brackets. Coating stability after friction testing was evaluated by SEM and XRD by all the studies except Shah et al.,[21] and only one study[13] evaluated the coating stability by manual bending test. All the included studies clearly demonstrated the coating method used to deposit the nanoparticles over archwires. Coating methods are specific for the chemical nature of the particular nanoparticles. For fullerene-like nanoparticles, electro-less deposition were used by two studies[13],[14] and electro-deposition by one study.[15] Compared to electroless deposition, which is frequently used electrodeposition has made the coating application more controllable and manageable and this is in agreement with the similar trails carried out by other studies. PBIID (Plasma-based ion implantation/deposition) and MCECR (Mirror- confinement- type electron cyclotron resonance) plasma sputtering was used by two studies[16],[18] and produced successful results while PVD (Physical vapour deposition) were used by few other studies.[17],[20],[21]

Future research and recommendations

All the 9 studies were in vitro experimental study; there are controversies among different investigators regarding the effects of the intraoral lubrication. Few studies claimed that wet conditions were ineffective on several materials.[37],[38] Only two studies[15],[18] compared the frictional behaviour of the coated wires in both dry and wet conditions, however the results obtained by them were extremely heterogeneous with other. According to the results and to the limited evidence provided by the literature further investigations are needed to understand the behaviour of the coated wires in a condition simulating oral environment. The use of coated orthodontic wires in routine orthodontic practice can be implemented only after in vivo human clinical trials. Since few studies have been done to evaluate other physical/mechanical properties, further studies are required to explore these properties. Only two of the nine studies investigated the effect of nanoparticle coating on brackets in frictional resistance at bracket wire interface,[18],[19] results obtained from these studies were inconclusive and future researches are recommended to strengthen the evidence.


  Conclusion Top


  1. Null hypothesis has been rejected according to our systematic review, and it can be concluded that overall coating of orthodontic archwires has a positive effect in terms of frictional resistance at bracket-wire interface under specified in-vitro conditions. Moreover, it is recommended that coated orthodontic wires in routine orthodontic practice can be used only after in vivo human clinical trials.
  2. Most of the studies were conducted over stainless steel arch wires and while comparing the frictional behaviour of coated stainless steel and other coated wires the former showed better performance in terms of frictional resistance after coating.
  3. Many methods have been used for coating of orthodontic wires producing reliable coating stability. PBIID (plasma-based ion implantation and deposition) and electrodeposition method can be successfully used to create a surface layer with consistent repeatability.
  4. During the reviewing process it is found that diamond like carbon (DLC) and fullerene like tungsten disulfide (IF-WS2) nanoparticles significantly reduce the friction of orthodontic arch wires up to 50% under different experimental conditions.
  5. Further studies are necessary to strengthen the evidence regarding effect of coated brackets on frictional properties at bracket-wire interface and effect of overall coating on other mechanical properties.


Abbreviations

SS (stainless steel), NiTi (nickel titanium), DLC (diamond like carbon), TiAlN (titanium aluminium nitride), WC/C (tungsten carbide), IF-WS2 (fullerene like tungsten disulfide), ZnO (zinc oxide), PBIID (Plasma- based ion implantation/deposition), MCECR (Mirror- confinement- type electron cyclotron resonance), PVD (Physical vapour deposition), SEM (scanning electron microscope), XRD (X-ray diffractometry), Gpa (gigapascals), Hv (Vickers hardness).

Financial support and sponsorship

Nil.

Conflicts of interest

There are no conflicts of interest.



 
  References Top

1.
Kusy P. Ongoing innovation in biomechanics and materials for the new millennium. Angle Orthod 2000;70:366-76.  Back to cited text no. 1
    
2.
Besancon RM. The Encyclopedia of Physics. 3rded. New York: Van Nostrand Reinhold Company; 1985.  Back to cited text no. 2
    
3.
Farrant SD. An evaluation of different methods of canine retraction. Br J Orthod 1976;4:5-15.  Back to cited text no. 3
    
4.
Kusy RP, Whitely JQ. Effect of surface roughness on the coefficients of friction in the model orthodontic systems. J Biomech 1990;23:913-24.  Back to cited text no. 4
    
5.
Kusy RP, Whitely JQ. Friction between different wire bracket configuration and materials. Semin Orthod 1997;3:166-77.  Back to cited text no. 5
    
6.
Kusy RP, Tobin EJ, Whitely JQ, Sioshanshi JQP. Friction coefficients of ion implanted alumina against ion implanted beta titanium in the low load, low velocity, single pass regime. Dent Mater 1992;8;167-72.  Back to cited text no. 6
    
7.
An engineer's guide to friction: Defense Metals Information Center, Batelle Memorial Institute, Columbus, Ohio, 1970, DMIC Memorandum 246.  Back to cited text no. 7
    
8.
Palmer F. Friction. Sci Am 1951;184:54-60.  Back to cited text no. 8
    
9.
Moher D, Liberati A, Tetzlaff J, Altman DG. The PRISMA Group. Preferred reporting items for systematic reviews and meta-analyses: The PRISMA statement. Int J Surg 2010;8:336–41.  Back to cited text no. 9
    
10.
Higgins JPT, Thomas J, Chandler J, Cumpston M, Li T, Page MJ, et al., (editors). Cochrane Handbook for Systematic Reviews of Interventions. London: Cochrane; 2019.  Back to cited text no. 10
    
11.
Soares FZM, Follak A, da Rosa LS, Montagner AF, Lenzi TL, Rocha RO. Bovine tooth is a substitute for human tooth on bond strength studies: A systematic review and meta-analysis of in vitro studies. Dent Mater 2016;32:1385-93.  Back to cited text no. 11
    
12.
AlShwaimi E, Bogari D, Ajaj R, Al-Shahrani S, Almas K, Majeed A. In Vitro Antimicrobial Effectiveness of Root Canal Sealers against Enterococcus faecalis: A Systematic Review. J Endod. 2016 Nov;42(11):1588-1597. doi: 10.1016/j.joen.2016.08.001. Epub 2016 Sep 9. PMID: 27623499.  Back to cited text no. 12
    
13.
Redlich M, Katz A, Rapoport L, Wagner HD, Feldman Y, Tenne R. Improved orthodontic stainless steel wires coated with inorganic fullerene-like nanoparticles of WS2 impregnated in electroless nickel – phosphorous film. Dent Mater 2008;24:1640-6.  Back to cited text no. 13
    
14.
Samorodnitzky GR, Redlich M, Rapoport L, Feldman Y, Tenne R. Inorganic fullerene-like tungsten disulfide nanocoating for friction reduction of nickel-Titanium alloys. Nanomedicine 2009;4;943-50.  Back to cited text no. 14
    
15.
Gracco A, Dandrea M, Deflorian F, Zanella C, Stefani AD, Bruno G, and Stellini E. Application of a Molybdenum and Tungsten Disulfide Coating to Improve Tribological Properties of Orthodontic Archwires. Nanomaterials. 2019;9:753.  Back to cited text no. 15
    
16.
Muguruma T, Iijima M, Brantley WA, and Mizoguchi I. Effects of a diamond-like carbon coating on the frictional properties of orthodontic wires. Angle Orthod. 2011; 81:141-148.  Back to cited text no. 16
    
17.
Zhang H, Guo S, Wang D, Zhou T, Wang L, Ma J. Effects of nanostructured diamond like carbon coating and nitrocarburizing on the frictional properties and biocompatibility of orthodontic stainless-steel wires. Angle orthod. 2016;86(5):782-8.  Back to cited text no. 17
    
18.
Kang T, Huang SY, Huang JJ, Li QH, Diao DF and Duan YZ. The effects of diamond like carbon films on fretting wear behavior of orthodontic archwire bracket contacts. J Nanosci Nanotechnol. 2015;15;4641–4647.  Back to cited text no. 18
    
19.
Behroozian A, Kachoei M, Khatamian M, Divband B. The effect of ZnO nanoparticle coating on the frictional resistance between orthodontic wires and ceramic brackets. J Dent Res Dent Clin Dent Prospect 2016;10:106-11.  Back to cited text no. 19
    
20.
Krishnan V, Ravikumar KK, Sukumaran KJ. In vitro evaluation of physical vapour deposition coated beta titanium orthodontic archwires. Angle orthod. 2012; 82:22-29.  Back to cited text no. 20
    
21.
Shah PK, Sharma P, Goje SK. Comparative evaluation of frictional resistance of silver-coated stainless steel wires with uncoated stainless steel wires: An In vitro study. Contemp Clin Dent. 2018; 9:331-6.  Back to cited text no. 21
    
22.
Tenne R, Margulis L, Genut M, Hodes G. Polyhedral and cylindrical structures of WS2. Nature 1992;360:444–5.Rapoport L, Leshchinsky V, Lapsker I, Volovik Y, Nepomnyashchy O, Lvovsky M, et al. Tribological properties of WS2 nanoparticles undermixed lubrication. Wear 2003;255:785–93.  Back to cited text no. 22
    
23.
Rapoport L, Leshchinsky V, Lapsker I, Yu Volovik, Nepomnyashchy O, Lvovsky M, et al. Tribological properties of WS2 nanoparticles undermixed lubrication. Wear. 2003;255:785-93.  Back to cited text no. 23
    
24.
Zou TZ, Tu JP, Zhang SC, Chen LM, Wang Q, Zhang LL, et al. Friction and wear properties of electroless Ni-P-(IF–MoS2) composite coating in humid air and vacuum. Mater Sci Eng 2006;426:162–8.  Back to cited text no. 24
    
25.
Redlich M, Mayer Y, Harari D, Lewinstein I. In vitro study offrictional force during sliding mechanics of ''reduced-friction'' brackets. Am J Orthod Dentofacial Orthop 2003;124:69–73.  Back to cited text no. 25
    
26.
Cha J, Kim K, Hwang C. Friction of conventional and silica insert ceramic bracket in various bracket-wire combinations. Angle Orthod 2007;77:100–7.  Back to cited text no. 26
    
27.
Cash A, Curtis R, Garrigia-Majo D, McDonald F. A comparative study of the static and kinetic frictional resistance of titanium molybdenum alloy archwires in stainless steel brackets. Eur J Orthod 2004;26:105–11.  Back to cited text no. 27
    
28.
Tsai, Pi-Chuen, Jueh-Yu Chiang, and Yen-Fei Hwang. “Characteristics and mechanical properties of titanium-containing diamond like carbon films deposited by cathodic arc evaporation.” Journal of nanoscience and nanotechnology 8.5 (2008): 2516-2521.  Back to cited text no. 28
    
29.
R. Said, N. Ali, C. A. A. Ghumman, O. M. N. D. Teodoro, and W. Ahmed Characterisation of DLC Films Deposited Using Titanium Isopropoxide (TIPOT) at Different Flow Rates. J. Nanosci. Nanotechnol. 9, 4298-4304(2009).  Back to cited text no. 29
    
30.
Huang, S. Y., Huang, J. J., Kang, T., Diao, D. F., & Duan, Y. Z. (2013). Coating NiTi archwires with diamond-like carbon films: reducing fluoride-induced corrosion and improving frictional properties. Journal of Materials Science: Materials in Medicine, 24(10), 2287–2292. doi:10.1007/s10856-013-4988-0.  Back to cited text no. 30
    
31.
Baker KL, Nieberg LG, Weimer AD, Hanna M. Frictional changes in force values caused by saliva substitution Am J Orthod Dentofacial Orthop 1987;91:316-20.  Back to cited text no. 31
    
32.
Muguruma T, Iijima T, Brantley WA, Nakagaki S, Endo K, Mizoguchi I. Frictional and mechanical properties of diamond-like carbon- coated orthodontic brackets. Eur J Orthod 2013;35:216-22.  Back to cited text no. 32
    
33.
K. Sridharan, S. Anders, M. Nastasi, K. C. Walter, A. Anders, O. R. Monteiro, and W. Ensinger, “Nonsemiconductor Applications of PIII&D,” in Handbook of Plasma Immersion Ion Implantation and Deposition, A. Anders, Ed., New York: Wiley, 2000, pp. chapter 10.  Back to cited text no. 33
    
34.
Fontaine J, Donnet C, Erdemir A. Fundamentals of the tribology of DLC coating. In: Donnet C, Erdemir A, editors. Tribology of Diamond-like Carbon Films. New York, NY: Springer; 2008. p. 139–54.  Back to cited text no. 34
    
35.
Omana HM, Moore RN, Bagby MD. Frictional properties of metal and ceramic brackets. J Clin Orthod 1992;26:425-32.  Back to cited text no. 35
    
36.
Kachoei M, Behroozian A. Comparison of friction between ceramic brackets and ZnO nanoparticle coated wires. Iran J Orthod 2010;5:77-84.  Back to cited text no. 36
    
37.
Kusy RP, Whitley JQ. Influence of fluid media on the frictional coefficients in orthodontic sliding. Semin Orthod 2003;9:281-9.  Back to cited text no. 37
    
38.
Pratten DH, Popli K, Germane N, Gunsolley JC. Frictional resistance of ceramic and stainless steel orthodontic brackets. Am J Orthod Dentofacial Orthop 1990;98:398-403.  Back to cited text no. 38
    


    Figures

  [Figure 1]
 
 
    Tables

  [Table 1], [Table 2], [Table 3], [Table 4]



 

Top
 
 
  Search
 
Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
Access Statistics
Email Alert *
Add to My List *
* Registration required (free)

 
  In this article
Abstract
Introduction
Materials and Me...
Results
Discussion
Conclusion
References
Article Figures
Article Tables

 Article Access Statistics
    Viewed706    
    Printed26    
    Emailed0    
    PDF Downloaded76    
    Comments [Add]    

Recommend this journal